Mani Schutz Dental (Germany)
Capo Bond

Packing: 5ml

  • Total etch all in one.
  • Optional Capo Bond Activator to wake dual cure.
  • Dual-curing 20 MPa.
Capo Bulk Fill

Packing: 2g Syringe

Indications:
  • Fillings with a layer thickness of up to 4 mm in Black’s class I and II cavities.
  • Cavity lining as a first (lowermost) layer in Black’s class I and II cavities.
Advantages:
  • Quick and easy handling with layer thicknesses of up to 4 mm.
  • Minimal shrinkage = safe application.
  • Exceptional physical properties (filler content ca. 77%).
  • High radiopacity (210% al).
  • Compatible with most bonders and composites.
  • Biocompatible: 100% free of bisphenol A, HEMA and TEG-DMA.
  • Universal dentin color = natural appearance.
  • Easy to polish.
Youngs modulus: 11,090 MPa
Bending strength:  134 MPa
Vickers hardness: 740 Mpa
Compressive strength: 381 MPa
Volume Shrinkage: 2.9%
Radiopacity: 210% Al
Filler Content: 77 weight-%
Available Shade:
Universal dentin color.
Capo Flow

Packing: 2g Syringe

Flowable dentistry composite on micro-hybrid basis for cavity linings, filling small defects and sealing fissures.

Youngs modulus: 6,998 MPa
Bending strength:  134 MPa
Vickers hardness: 374 Mpa
Compressive strength: 403 MPa
Available Shades:
A1, A2, A3, A3.5, A4, B2, B3 & C3.
Capo Natural

Packing: 4g Syringe

Indications:
  • Direct posterior and anterior tooth restorations in Black’s classes I, II, III, IV and V.
  • Minimally invasive veneers and fillings.
  • Extended fissure sealing of molars and premolars.
  • Splinting loosened teeth.
Advantages:
  • High abrasion resistance combined with being antagonist-friendly.
  • Outstanding polishing behavior.
  • Excellent mechanical properties.
Youngs modulus: 11,861 MPa
Bending strength:  144 MPa
Vickers hardness: 685 Mpa
Compressive strength: 452 MPa
Available Shades:
A1, A2, A3, A3.5, A4, Incisal Medium, Incisal Clear, Incisal White, Bleach 1, Bleach 2, B2, B3, C2, C3 & Universal Shade.
Capo Universal

Packing: 6g Syringe

Indications:
  • Direct posterior and anterior tooth restorations in Black’s classes I, II, III, IV and V.
  • Minimally invasive veneers and fillings.
  • Extended fissure sealing of molars and premolars.
  • Splinting loosened teeth.
Advantages:
  • High abrasion resistance combined with being antagonist-friendly.
  • Outstanding polishing behavior.
  • Excellent mechanical properties.
Youngs modulus: 11,861 MPa
Bending strength:  144 MPa
Vickers hardness: 685 Mpa
Compressive strength: 452 MPa
Available Shade:
Universal Shade.
NanoPaq

Packing: 4g Syringe

Indications:
  • Direct anterior and posterior tooth restorations in Black’s classes I, II, III, IV and V.
  • Minimally invasive veneers and fillings.
  • Splinting loose teeth.
  • Corrections of enamel color and tooth shape to improve aesthetics.
Advantages:
  • Extremely low shrinkage.
  • Easy handling.
  • Very high compressive strength of 462 MPa.
  • Ideal for minimally invasive techniques.
  • Easy to polish.
Youngs modulus: 18,154 MPa
Bending strength:  152 MPa
Vickers hardness: 1,088 Mpa
Compressive strength: 462 MPa
Volume Shrinkage: 1.3%
Available Shades:
A1, A2, A3, A3.5, A4, B1, B2, B3, OD A2, OD B2, IW, InTr, C2, IR, InU, InBI & D3.